Investigation of Laser, Wire-cut and Plasma Cutting Methods on the Residual Stress Distribution of St37 Sheet Using the Contour Method

Document Type : Research Paper

Authors

Department of Mechanical Engineering, University of Kashan, Kashan, Iran

Abstract

Cutting is one of the most important manufacturing processes in various industries. After the cutting process, residual stresses are created in different parts. Hence, the calculation and prediction of residual stresses is important and ignoring such a matter when combined with applied stresses can cause failure in parts. In this study, the effects of laser, plasma and wire-cut processes were investigated on the residual stress of st37 sheet using the contour method. For this purpose, an experiment with 8 operational steps including 3 sets of st37 sheets with thicknesses of 4, 6 and 8 mm in the dimensions of 100 × 100 mm2 were prepared and, after the stress relief operation, cut by the mentioned cutting methods. After the cutting processes were conducted and the temperatures were recorded with a laser thermometer, the test specimens were prepared for the contour method. According to the results, the highest residual stress was caused due to laser cutting in the sample with a thickness of 4 mm and its value is 142 MPa. The lowest residual stress obtained in wire-cut cutting and its value was 28 MPa. As the thickness increased, the amount of residual stress decreased in all methods. The slope of the temperature changes of the part from the moment of cutting to the ambient temperature is higher in laser cutting and the residual stress in this method is higher than the plasma and wire cut method.

Keywords


[1]    M. Alinaghian, I. Alinaghian, M. Honarpisheh, Residual stress measurement of single point incremental formed Al/Cu bimetal using incremental hole-drilling method, International Journal of Lightweight Materials and Manufacture, 2(2) (2019) 131-139.
[2]    M. Sedighi, M. Honarpisheh, Investigation of cold rolling influence on near surface residual stress distribution in explosive welded multilayer, Strength of Materials, 44(6) (2012) 693-698.
[3]    M. Honarpisheh, E. Haghighat, M. Kotobi, Investigation of residual stress and mechanical properties of equal channel angular rolled St12 strips, Proceedings of the Institution of Mechanical Engineers, Part L: Journal of Materials: Design and Applications, 232(10) (2018) 841-851.
[4]    M. Kotobi, M. Honarpisheh, Uncertainty analysis of residual stresses measured by slitting method in equal-channel angular rolled Al-1060 strips, The Journal of Strain Analysis for Engineering Design, 52(2) (2017) 83-92.
[5]    M. Moazam, M. Honarpisheh, Ring-core integral method to measurement residual stress distribution of Al-7075 alloy processed by cyclic close die forging, Materials Research Express, 6(8) (2019).
[6]    A. Aghababaei, M. Honarpisheh, Experimental and numerical investigation of residual stress distribution in Al-6061 tubes under using tubular channel angular pressing process by new trapezoidal channel, The Journal of Strain Analysis for Engineering Design, (2022).
[7]    M. Moazam, M. Honarpisheh, Improving the mechanical properties and reducing the residual stresses of AA7075 by combination of cyclic close die forging and precipitation hardening, Proceedings of the Institution of Mechanical Engineers, Part L: Journal of Materials: Design and Applications, 235(3) (2021) 542-549.
[8]    M. Tavajjohi, M. Honarpisheh, Experimental and numerical study of the longitudinal and transverse residual stresses distribution in the constrained groove pressing process of pure copper sheets, Proceedings of the Institution of Mechanical Engineers, Part L: Journal of Materials: Design and Applications, 236(1) (2022) 97-109.
[9]    I. Alinaghian, M. Honarpisheh, S. Amini, The influence of bending mode ultrasonic-assisted friction stir welding of Al-6061-T6 alloy on residual stress, welding force and macrostructure, The International Journal of Advanced Manufacturing Technology, 95(5) (2018).
[10]    M.B. Prime, Cross-sectional mapping of residual stresses by measuring the surface contour after a cut, J. Eng. Mater. Technol., 123(2) (2001) 162-168.
[11]    P. Pagliaro, M. Prime, B. Zuccarello, Multiple stress components from multiple cuts for the contour method, in Proceedings of the XXXV AIAS Conference, (2006) 13-16.
[12]    P. Pagliaro, M.B. Prime, H. Swenson, B. Zuccarello, Measuring multiple residual-stress components using the contour method and multiple cuts, Experimental mechanics, 50(2) (2010) 187-194.
[13]    M.B. Prime, D.J. Hughes, P.J. Webster, Weld application of a new method for cross-sectional residual stress mapping, in SEM Annual conference on experimental and applied mechanics, Portland, Oregon, ASM, (2001) 608-611.
[14]    M.B. Prime, R.L. Martineau, Mapping residual stresses after foreign object damage using the contour method, in Materials Science Forum, 404 (2002) 521-526.
[15]    M.B. Prime, M.A. Newborn, J.A. Balog, Quenching and cold-work residual stresses in aluminum hand forgings: contour method measurement and FEM prediction, Los Alamos National Lab.(LANL), Los Alamos, NM (United States), (2003).
[16]    M.B. Prime , A. L. Kastengren, The contour method cutting assumption: error minimization and correction, in Experimental and Applied Mechanics, 6 (2011) 233-250.
[17]    Y. Zhang, S. Pratihar, M.E. Fitzpatrick, L. Edwards, Residual stress mapping in welds using the contour method, in Materials science forum, 490 (2005) 294-299.
[18]    N. Murugan and R. Narayanan, Finite element simulation of residual stresses and their measurement by contour method, Materials & Design, 3(6) (2009) 2067-2071.
[19]    R. Dennis, D. Bray, N. Leggatt, M. Turski, Assessment of the influence of plasticity and constraint on measured residual stresses using the contour method, in ASME Pressure Vessels and Piping Conference, 48296 (2008) 477-485.
[20]    A. Arif, B. Yilbas, B. A. Aleem, Laser cutting of thick sheet metals: Residual stress analysis, Optics & Laser Technology, 41 (3) (2009) 224-232.
[21]    A. Arif, B. Yilbas, “Modelling of residual stresses during laser cutting of small-diameter holes," SAGE Journals, vol. 222, (2008).
[22]    M. Harničárová, J. Valíček, A. Öchsner, R. Grznárik, M. Kušnerová, J. Neugebauer, D. Kozak, Predicting residual and flow stresses from surface topography created by laser cutting technology, Optics & Laser Technology, 52 (2013) 21-29.
[23]    B. Yilbas, S. Akhtar, C. Karatas, Laser cutting of alumina tiles: Heating and stress analysis, Journal of Manufacturing Processes, 15(1) (2013) 14-24.
[24]    E. Salvati, A. Korsunsky, Micro-scale measurement & FEM modelling of residual stresses in AA6082-T6 Al alloy generated by wire EDM cutting, Journal of Materials Processing Technology, 275 (2020).
[25]    P.S. Rao, K. Ramji, B. Satyanarayana, Effect of wire EDM conditions on generation of residual stresses in machining of aluminum 2014 T6 alloy, Alexandria Engineering Journal, 55(2) (2016) 1077-1084.
[26]    S. Kumar, S. Grover, R. Walia, Effect of hybrid wire EDM conditions on generation of residual stresses in machining of HCHCr D2 tool steel under ultrasonic vibration, International Journal on Interactive Design and Manufacturing (IJIDeM), 12(3) (2018) 1119-1137.
[27]    S. Bhattacharya et al., Simulation of residual stress using thermomechanical analysis on wire EDM cut surface, Materials Today: Proceedings, 19 (2019) 462-467.
[28]    B. Ekmekci, Residual stresses and white layer in electric discharge machining (EDM), Applied surface science, 253(23) (2007) 9234-9240.
[29]    B. Ekmekci, A. E. Tekkaya, A. Erden, A semi-empirical approach for residual stresses in electric discharge machining (EDM), International Journal of Machine Tools and Manufacture, 46 (2006)
[30]    T. Arai, G. Baker, C. Bates, B. Becherer, ASM Handbook, Vol. 4: Heat Treating. ASM International, (1991) 448, 845.